DESCRIPTION
Epo-Crete WB Gloss is a high solids non-yellowing Water Based Epoxy-Acrylic sealer designed for interior concrete sealing applications such as stamped, stenciled, cementitious overlays, acid stained and brushed or trowel finished concrete surfaces. Epo-Crete WB Gloss is usually used on horizontal surfaces only.
APPLICATION INSTRUCTIONS:
SURFACE PREPARTAION: Concrete surface must be clean and free of all contaminants and water. Do not apply if moisture could be present within 24 hours. If moisture is present or if the surface is not clean and free of all contaminants, the sealer may have white spots and have premature delamination and failure.
Substrate temperature must be no less than 50 degrees F and not exceed 85 degrees F. If applied outside these limits the sealer may not achieve adequate film formation and may have excessive air entrapment, bubbles, blushing or hazing.
MIXING: Stir well before using. Material may separate during long term storage.
APPLICATION: Apply using a 3/8" - 1/2" nap roller cover using long even uniform strokes at approximately 200-350 square feet per gallon depending on porosity and texture of substrate. A hand held pump up style sprayer may be used as well (back rolling may be necessary when spraying). Do not allow to Puddle! Thick or puddle areas may prevent the water from evaporating and may be susceptible to moisture intrusion which may cause milky white spots. Applying too thin may cause sealer to prematurely delaminate, flake or wear away. Allow sealer to dry for 24 hours for light traffic and at least 48 hours for heavy traffic. If applying two coats, wait approximately 4 - 6 hours between coats.
PLEASE NOTE: It is always recommended to test the product in a small, inconspicuous area (on the same concrete substrate) for desired results prior to application. Coverage rates may vary for all coatings and substrates depending on porosity, density, texture etc. If applying by spray method, extended coverage rates may be achieved, but be aware that less material will be applied and inadequate film formation or performance expectations may be limited.